Sifat Optoelektronik Ws2 Yang Dimodifikasi Dengan Metode Eksfoliasi Fase Cair

Abstract

Abstrak pada tugas akhir ini penulis melakukan penelitian dengan tujuan untuk mengamati sifat listrik dan sifat optolektronik lapisan tipis WS2. WS2 dimodifikasi dengan eksfoliasi fase cair. Karakterisasi dilakukan dengan mengamati kurva I-V saat sebelum diberi gangguan, saat diberi gangguan dan setelah diberi gangguan eksternal berupa cahaya. Hasil karakterisasi kurva I-V WS2 yang dideposisi diatas substrat polyethylene terephthalate (PET) menunjukkan secara umum WS2 bersifat insulator dengan fluktuasi nilai arus di sebagian sampel. Arus yang mengalir pada sampel sebelum diberi cahaya sebesar -0.87 sampai 1.24 nA saat tegangan divariasi dari -5 sampai 5 V dengan nilai resistansi 3.6842 GΩ. Setelah tidak diberi cahaya nilai arus berubah menjadi -0.61 sampai 0.717 nA dengan nilai resistansi 6.59 GΩ. Nlai arus saat diberi cahaya mengalami fluktuasi dan perlu diteliti lebih lanjut. Selain itu, pada penelitian ini dilakukan juga karakterisasi Raman, photoluminescence (Pl) dan Uv-Vis. Hasil karkaterisasi Raman menunjukkan sampel masih berbentuk multilayer dengan munculnya puncak vibrasi E 1 2g(Γ) pada 354.9 cm-1 dan A1g(Γ) pada 420 cm-1 dengan selisih 65.1 cm-1 . Hasil karakterisasi Pl muncul pada puncak 650 nm menandakan adanya kontribusi eksiton pada sampel multilayer. Karakteriasi Uv-Vis pada puncak exciton A 638.2 dan B 530.6 nm menandakan WS2 masih tersusun dalam multilayer. Kata Kunci: WS2, eksfoliasi fase cair, Sifat Listrik, sifat optoelektronik, Raman spektroskopi, Photoluminiscence Abstract In this final task, the authors studies the optoelectronic properties of the WS2 thin layer. The WS2 is modified with liquid-phase exfoliation and deposited on top of the polyethylene terephthalate (PET) substrate. The I-V characteristic curves were observed before and after light illumination as well as when the sample was illuminated by the green light. In general, the WS2 thin film shows insulating behavior. The current was observed to be fluctuated in several samples. Without light illumination, the currents were -0.87 to 1.24 nA when the voltage was varied from -5 to 5 V. The current resistance is about 3.6842 GΩ. After light illumination, the current changes to -0.61 to 0.717 nA with a resistance value of 6.59 G Ω. Light induces current fluctuation in several samples. Besides, the samples were also characterized by Raman, photoluminescence, and Uv-Vis spectroscopy. of the multilayer characteristics is evidenced by the vibration peaks of E1 2g(Γ) at 354.9 cm-1 and A1g(Γ) at 420 cm-1 with a difference of 65.1 cm-1. A photoluminescence peak of 650 nm indicates the contribution of exciton in multilayer samples. The Uv-Vis characterization at peaks A 638.2 and B 530.6 nm also suggests that the WS2 thin film is still composed in multilayers. Keywords: WS2, liquid phase, electrical properties, optoelectronic properties, Raman spectroscopy, Photoluminescence